Environmentally Friendly Rubber to Metal/Steel Adhesive Thinkbond
94S
Product Description:
THINKBOND 94S is a thermoreactive adhesive for bonding silicone
elastomers (VMQ), PU with steel, aluminum, aramid, textile fibers
and glass by vulcanization process. The textile fibers can be:
Cotton, cellulose, polyamide, polyester and aramid. This adhesive
is also used to promote adhesion between the elastomer and
chemically treated surfaces which cannot be grit blasted such as:
Phosphate steel, galvanized, chromate conversion treated and
stainless, moreover ceramic engineering. THINKBOND 94S is a heavy
metals free product.
Features:
- Appearance : Clear to light yellow liquid.
- Non-volatile solids (2h @ 70°C) : 12-18 %
- Density at 25°C : 0,84-0.88 g/cm3
- Viscosity Brookfield at 25°C : 10 cps - #2 spindle @ 30 rpm.
- Viscosity Ford Cup # 4 at 25°C : 12 s.
- Diluents : Methanol/ Ethanol 99º GL
- Bonding Temperature Range : 150 to 200ºC
- Shelf life : 2 years (closed can below 25ºC).
Technical Parameters:
| Technical Parameter | Value |
|---|
| Name | Rubber to metal adhesive |
| Appearance | Clear to light yellow liquid |
| Diluents | Methanol/ Ethanol 99º GL |
| Type | Liquid |
| Odor | Solvent |
| Packaging | 25L, 200L |
| Application | Rubber to metal bonding |
| Shelf life | 2 years |
| Environmentally Friendly | Yes |
| Dilutable | Yes |
| Universal Bonding Agent | Yes |
Applications:
HOW TO PREPARE THE SURFACE: Prepare the metal surface properly by removing completely oil,
grease and dirt. Blasting the surface with grit blasting steel so
that the surface roughness is greater than 15 µm. For aluminum
surfaces, we recommend the use of aluminum oxide as abrasive. Clean
again the substrate to remove dust from blasting residues.
THINKBOND 94S can be applied on surfaces treated by chemical
processes such as galvanizing, phosphating, KTL... For the
application as an adhesion promoter, we recommend to apply
THINKBOND 94S above smooth and dry metal. Then you should apply the
suitable adhesion system to the elastomer.
APPLICATION: Agitation: We recommend stir THINKBOND 94S before the application to avoid
sedimentation.
Dilution: Dilution of the product depends on the applications methods. We
recommend that dilution is always made with Methanol or Ethanol 99º
GL. After dilution is recommended use all diluted product in the
same day to avoid the hydrolysis reaction with possible
decantation.
Dipping: For this application, we recommend diluting between 100 and 500%
v/v.
Brushing: For this application, we recommend diluting between 100 and 500%
v/v. Spray: For this application, we recommend diluting between 100 and 500%
v/v.
Application Layer: The film obtained by applying THINKBOND 94S is extremely thin and
colorless. The layer thickness must be between 1 and 4 µm.
THINKBOND 94S is very reactive so we recommend that parts with
THINKBOND 94S are cured the same day of the application.
Drying: Dry film between 10 and 30 minutes at room temperature. If it is
necessary to reduce drying time, we recommend using forced air for
2 minutes at 65ºC maximum.
For drying, do not use process temperatures above 82ºC in order to
avoid adhesive pre-cure. After this process, follow instructions to
vulcanization.
Containers – Available in 4L, 18L and 200L UN approved containers.
Safe Handling Information – Refer to the Material Safety Data Sheet for THINKBOND 94S before
using, handling or storing. This product is for commercial use only
and should be applied by trained personnel.
Shanghai LoreChem Co., Ltd. was established in 2008. It is a
high-tech enterprise which is dedicated to serve releasing products
which involve semi-permanent release agent, anti-sticking, surface
lubrication and thermal reactive adhesive. Shanghai LoreChem has
been improving product quality for 15 years. The releasing products
are mainly applied in rubber, polyurethane and composite industry.
The brand of Lubekote for release agent and Thinkbond for adhesive
have been registered in China. Both of them are well known in the
industry.
Shanghai LoreChem 's business is all over the domestic and foreign
high-end production enterprises by providing professional technical
solutions and services. The company's long-term goal is to become
one of the best suppliers of release agent in Asia.